Co-precipitation of yttrium and barium fluorides from aqueous solutions

Co-precipitation of barium and yttrium fluorides from aqueous solutions at room temperature produced non-equilibrium Ba1−xYxF2+x nanofluoride phase with face-centered cubic crystal lattice of fluorite-type with the composition interval of the homogeneity for x = 0.35–0.75. Lattice parameter a of this solid solution nanophase varied as a function of the sample chemical composition in a complex manner with two areas of linear dependency, from x = 0.35 to 0.45 and from x = 0.50 to 0.75. A plausible explanation of this phenomenon included a change of the type of crystal lattice defects and the manner of their population with the corresponding ions. An increase of the relative amount of yttrium in the HF reaction system led to the formation of hydroxonium salt of decafluorotriyttrium acid, (H3O+)Y3F10−·nH2O, instead of expected YF3 hydrate. No formation of oxyfluoride phases under acidic conditions has been observed.