Title of article
Crystal growth of the neodymium-rich Nd1+xBa2-xCu3Oz solid solution
Author/Authors
Goodilin، نويسنده , , E. and Kambara، نويسنده , , M. and Umeda، نويسنده , , James T. P. Yao، نويسنده , , X. and Shiohara، نويسنده , , Y.، نويسنده ,
Issue Information
روزنامه با شماره پیاپی سال 1998
Pages
8
From page
54
To page
61
Abstract
In the present work on the basis of experimental phase relations in the copper-rich corner of the Nd-Ba-Cu-O system, the insulating Nd1+xBa2-xCu3Oz solid solution single crystals, with x = 0.43–0.85, were grown by the top-seeded-solution-growth method. The as-grown Nd1.85Ba1.115Cu3Oz crystals were found to be orthorhombic. As a result, the twin-like structure was observed and the twin-plane re-entrant-edge (TPRE) crystal growth mechanism was proposed.
Keywords
Crystal growth , Solid solution , Top-seeded-solution-growth method
Journal title
MATERIALS SCIENCE & ENGINEERING: B
Serial Year
1998
Journal title
MATERIALS SCIENCE & ENGINEERING: B
Record number
2133158
Link To Document