Fracture toughness of polycrystalline tungsten under mode I and mixed mode I/II loading

The fracture toughness of swaged polycrystalline tungsten was tested parallel and perpendicular to the swaging direction and under mixed mode I/mode II loading. The fracture mode is dominated by the microstructure and changed from all-transgranular cleavage in mode I to almost all-intergranular fracture in mode II. The mixed mode results can be related to two common failure criteria, the maximum tensile stress criterion (Maximum σ) and the maximum energy release rate criterion (Maximum G), but the large scatter in the data prohibits a clear distinction between the two criteria. Tests at 77 K show that the polycrystal is significantly tougher than the single crystal at this temperature. This is a consequence of the deflection of the crack into the grain boundaries and the imperfect texture (as compared to a single crystal) of the polycrystalline material.