Desorption of LiAlH4 with Ti- and V-based additives

Thermal desorption spectroscopy and X-ray diffraction experiments show that ball-milling of LiAlD4 in presence of VCl3 or TiCl3·1/3(AlCl3) can reduce its thermal decomposition temperatures by 60 and 50 °C, respectively. However, some partial decomposition of LiAlD4 into Li3AlD6, Al and D2 occurs during the mechanical processing: 80% for TiCl3·1/3(AlCl3), 40% for VCl3. LiCl is formed during the ball-milling, this suggests the reduction of the additives by LiAlD4. The localisations of Ti or V atoms are not yet determined.