Microstructure evolution and texture development during high-temperature uniaxial compression of magnesium alloy AZ31

Texture development in magnesium alloy AZ31 was studied by uniaxial compression tests at temperatures, strain rates and final strains ranging from 573 to 773 K, 1.0 × 10−3 to 5.0 × 10−5 s−1 and −0.2 to −1.5, respectively. Fiber texture was formed in all of the deformation conditions. The main component of the texture varied depending on deformation conditions; it appeared about 33–38° away from the basal pole after the deformation at higher temperatures and lower strain rates. This can be attributed to the increased activity of the secondary pyramidal slip system. With a decrease in temperatures and an increase in strain rate, the tilting angle of the main component (compression plane) from the basal pole decreased down to about 20°. Construction of a basal fiber texture was detected after deformations at the lowest temperature and high strain rates.