Texture evolution and fraction of favorably oriented fibers in commercially pure aluminum processed to 16 ECAP passes

Texture evolution in 1050 commercial purity aluminum severely deformed by equal channel angular pressing (ECAP) is investigated by electron back scattered diffraction (EBSD). Pole figures and orientation distribution function (ODF) plots are generated for samples processed to 1, 2, 4, 8, 12 and 16 passes. The processing was done using route BC, in which the samples were rotated by 90° in the same sense between subsequent pressings. Two different sized scans were performed on the flow plane of the processed samples. The orientations constituting the favorably oriented fibers are depicted and crystal orientation maps are generated. The spatial distribution of grains having these orientations are revealed through these maps. The fraction of the main texture fibers for a 5° spread around the specified orientations is experimentally calculated and a quantitative idea on the evolution of texture is presented. The results ascertained that the texture intensity around the main fibers generally weakens with number of ECAP passes.