Flow behavior and microstructures of superalloy 718 during high temperature deformation

Flow behavior and microstructures of superalloy 718 were investigated by hot compression tests performed at temperatures ranging from 950 to 1100 °C with strain rates of 10−3 to 1 s−1. The dependence of the peak stress on deformation temperature and strain rate can be expressed by a hyperbolic-sine type equation. The activation energy for superalloy 718 is determined to be 443.2 kJ mol−1. A power exponent relationship between the peak strain and the Z parameter is obtained. Microstructure analysis shows that the dynamically recrystallized grain size is inversely proportional to the Z parameter. The nucleation mechanisms of DRX are closely related to the value of Z parameter. Under low Z conditions, DRX nucleation and development are mainly assisted by the formation of twins near the original grain boundaries.