Microstructure evolution associated with adiabatic shear bands and shear band failure in ballistic plug formation in Ti–6Al–4V targets

The microstructures and microstructure evolution associated with adiabatic shear band (ASB) formation in ballistic plugging in thick (2.5 cm) Ti–6Al–4V targets impacted by cylindrical, 4340 steel projectiles (2.0 cm in height) at impact velocities ranging from 633 m/s to 1027 m/s (just above the ballistic limit) were investigated by optical and transmission electron microscopy. ASB width increased from 10 μm to 21 μm as the velocity increased. ASB evolution was accompanied by the evolution of dark deformation bands composed of α′ martensite platelets which increased in density with increasing impact velocity. The corresponding Vickers microindentation hardness also increased from HV 619 to HV 632 in contrast to the surrounding matrix microindentation hardness of HV 555. These deformation bands were not necessarily precursors to ASB formation. The ASB average Vickers microindentation hardness was essentially constant at HV 645, a 16% increase over the matrix. This constant microindentation hardness was characterized by a consistent DRX grain structure which varied from equiaxed, defect-free grains (∼2 μm diameter) to heavily dislocated, equiaxed grains. Cracks nucleating and propagating within the ABSs were observed to increase from 8% to 87% of the ASB length with increasing impact velocity.