In situ observation of tensile deformation of high-pressure die-cast specimens of AM50 alloy

In situ observation of HPDC AM50 alloy in the SEM chamber was performed to study the changes of the micro-voids and the β phase during tensile deformation. The results suggested that micro-voids had little change in the elastic region, opened linearly with increasing load in the plastic region and led to final fracture. The detachment of β phase from the interface was also observed in the plastic region and there was no evidence to suggest that the detachment led to the final fracture.