Effect of NiCrAlY platelets inclusion on the mechanical and thermal shock properties of glass matrix composites

NiCrAlY platelets modified glass matrix composites were prepared. Their microstructures were characterized, their Youngʹs modulus, fracture strength in bending, Vickers hardness, and indentation toughness were measured, and their thermal shock resistance was studied using quenching-strength and indentation-quench methods. With increasing NiCrAlY content, evident enhancements of the Youngʹs modulus and indentation toughness were obtained. The NiCrAlY alloy inclusion could exert significant influences on the retained bending strength of the samples after quench tests, from 9.6 MPa for NiCrAlY-free glass to 32.0 MPa for 30 wt.% NiCrAlY-containing composites. The indentation-quench tests showed that NiCrAlY alloy inclusion elevated the critical quenching temperatures for propagation of pre-crack, from 150 °C for NiCrAlY-free glass to 225 °C for 30 wt.% NiCrAlY-containing composites. Inclusion debonding and intersection, crack deflection and bridging were observed, and are likely the micromechanisms accounted for the improvement of fracture resistance.