Preparation and characterisation of radiation hard PbWO4 crystal scintillator

The selective loss of one of the crystal constituents is found to be responsible for the yellowish coloration of PbWO4 crystals. However, using the already pulled crystals as the starting charge for the subsequent growth, colorless crystals can be grown. The crystals exhibiting excellent transmission characteristics have been grown employing a low temperature gradient, a moderate rotation rate of 15 rpm and a pull speed of 1 mm/h. The colored crystals show some radiation damage on gamma irradiation, while the colorless ones remain unaffected even for irradiation doses as high as 10 Mrad. Both the types of crystals show the presence of weak thermoluminescence (TL) emission when high irradiation doses (∼10 Mrad) are given. Only one TL glow peak is obtained in both the cases but the peak temperatures are different. The emission centers responsible for the TL emission are found to be the ones which give rise to the scintillation emission in the crystal.