A dual analysis for recycled particulate composites: linking micro- and macro-mechanics

The large amount of disposable bottles produced nowadays makes imperative the search for alternative procedures for recycling them since they are not biodegradable. This paper takes into consideration the thermomechanical recycling of post-consumed plastic bottles, especially the ones made of polyethylene terephthalate (PET) and high-density polyethylene (HDPE), and their use as composite materials for engineering applications. As changes on the compositeʹs microstructure can have an influence on macroscopic behavior, a new type of analysis is needed. To be able to evaluate the composite performance, a dual analysis procedure was developed. It consists of a micro-mechanical analysis where the microstructure is observed by optical microscopy, and variations in morphology are related to composite overall mechanical behavior. The macro-mechanical analysis is performed by ASTM D 3039/3039 M tensile tests. By doing this, the composite effective moduli can be determined. The new composite seems to be encouraging, i.e., an HDPE/PET composite with 40:60 ratio, in weight, experiments a stiffness recovery from the third to the fourth recycle. Moreover, the dual analysis was able to capture this variation.