Effect of surface pre-treatments on the zirconia ceramic–resin cement microtensile bond strength

Objective luate the influence of different surface treatments on the microtensile bond strength of resin cement to zirconia ceramic. als and methods cylinder-shaped (∅ 12 × 5.25 mm high) blocks of a commercial zirconium-oxide ceramic (Cercon® Zirconia, DENTSPLY) were randomly divided into 4 groups (n = 3), based on the surface treatment to be performed: (1) airborne particle abrasion with 125 μm Al2O3 particles (S); (2) selective infiltration etching (SIE); (3) experimental hot etching solution applied for 30 min (ST) and (4) no treatment (C). Paradigm MZ100 blocks (3M ESPE) were cut into twelve cylinders of 4 mm in thickness. Composite cylinders were bonded to conditioned ceramics using a resin cement (Calibra®, DENTSPLY), in combination with the proprietary adhesive system. After 24 h bonded specimens were cut into microtensile sticks and loaded in tension until failure. Bond strength data were analyzed with Kruskall–Wallis and Dunnʹs Multiple Range test for multiple comparisons (p < 0.05). Failure mode distribution was recorded and the interfacial morphology of debonded specimens was analyzed using a scanning electron microscope (SEM). s trength values achieved after SIE and ST treatment were significantly higher than after S treatment and without any treatment (p < 0.05). Premature failures were mostly recorded in the S group. icance ioning the high-strength ceramic surface with SIE and ST treatments yielded higher bond strengths of the resin cement than when zirconia ceramic was treated with airborne particle abrasion or left untreated.