Oxygen diffusion in zircon

Oxygen diffusion in natural, non-metamict zircon was characterized under both dry and water-present conditions at temperatures ranging from 765°C to 1500°C. Dry experiments were performed at atmospheric pressure by encapsulating polished zircon samples with a fine powder of18O-enriched quartz and annealing the sealed capsules in air. Hydrothermal runs were conducted in cold-seal pressure vessels (7–70 MPa) or a piston cylinder apparatus (400–1000 MPa) on zircon samples encapsulated with both18O-enriched quartz and18O water. Diffusive-uptake profiles of18O were measured in all samples with a particle accelerator, using the18O(p, α)15N reaction. For dry experimental conditions at 1100–1500°C, the resulting oxygen diffusivities (24 in all) are well described by:Ddry (m2/s) = 1.33 × 10 −4exp(−53920/T) There is no suggestion of diffusive anisotropy. wet conditions at 925°C, oxygen diffusion shows little or no dependence uponPH2O in the range 7–1000 MPa, and is insensitive to total pressure as well. The results of 27 wet experiments at 767–1160°C and 7–1000 MPa can be described a single Arrhenius relationship:Dwet (m2/s) = 5.5 × 10−12exp(−25280/T) sensitivity of oxygen diffusion toPH2O means that applications to geologic problems can be pursued knowing only whether the system of interest was ‘wet’ (i.e.,PH2O > 7MPa) or ‘dry’. Under dry conditions (presumably rare in the crust), zircons are extremely retentive of their oxygen isotopic signatures, to the extent that δ18O would be perturbed at the center of a 200 μm zircon only during an extraordinarily hot and protracted event (e.g., 65 Ma at 900°C). Under wet conditions, δ18O may or may not be retained in the central regions of individual crystals, cores or overgrowth rims, depending upon the specific thermal history of the system.