Study on preparation of montmorillonite-based composite phase change materials and their applications in thermal storage building materials

Three composite phase change materials (PCMs) were prepared by blending butyl stearate, dodecanol and RT20 with an organically modified montmorillonite (MMT), respectively. After the three composite PCMs were characterized by DSC, it was indicated that the RT20/MMT composite PCM was a good candidate for building applications due to its large latent heat, suitable phase change temperature and good performance stability. Compared with RT20, the RT20/MMT composite PCM exhibited higher heat transfer efficiency and had good compatibility with gypsum due to the combination with MMT. The composite gypsum boards containing RT20/MMT composite PCM had the function of reducing building energy consumption by reducing the indoor temperature variation, and the function was enhanced with the increase in the mass ratio of the RT20/MMT composite PCM.