Constraint effects at brittle fracture initiation in a cast ferritic steel

The fracture resistance of a cast low carbon manganese ferritic steel intended for containers for spent nuclear fuel has been analysed by combining several approaches. Based on data from three-point bend specimens with shallow and deep cracks the effect of crack tip constraint at brittle fracture initiation has been followed. Q-parameter was used for the constraint quantification. The crack length effect on the fracture toughness–temperature diagram has been analysed and peculiarities of fracture behaviour in the lower shelf region have been explained. The role of cleavage fracture stress in brittle fracture initiation under the influence of crack tip constraint has been analysed.