Shrinkage and desiccation cracking in bentonite–sand landfill liners

Data are reported on the shrinkage and desiccation cracking exhibited by bentonite-enhanced sand mixtures (BES) upon air-drying. Mixtures containing 10 and 20% bentonite by dry weight, compacted at moisture contents ranging from 8 to 32%, were investigated. Hydraulic conductivity data for BES specimens saturated and tested immediately after compaction, and for similar specimens that had no visible damage after air-drying, are also presented. e mixtures exhibited volumetric shrinkage upon air-drying with the amount of shrinkage increasing with increasing moisture content during compaction. At any initial moisture content mixtures containing 20% bentonite shrink more than those containing 10% bentonite, but the shrinkage is insensitive to the compactive effort. Compacted beds of BES containing 10 and 20% bentonite exhibit no visible desiccation cracking as the top surface is dried when compacted at 15 and 14% moisture content, respectively, and only minor cracking when compacted at initial moisture contents of 20 and 15%, respectively. For the range of mixtures tested, it appears that cracking only occurs when BES undergoes more than about 4% volumetric shrinkage when air-dried. The saturated hydraulic conductivity of intact BES specimens is unaffected by a drying episode prior to testing.