Development of anti-corrosion coating on low activation materials against fluoridation and oxidation in Flibe blanket environment

W coating by vacuum plasma spray process and Cr coating by chromizing process were performed on fusion low activation materials, JLF-1 ferritic steel and NIFS-HEAT-2 vanadium alloy. The present study discusses feasibility of the coatings as anti-corrosion coating against fluoridation in Flibe for fusion low activation materials. Coatings were characterized by microstructural analysis and examination on chemical stability by corrosion tests. The corrosion tests were conducted with H2O–47% HF solution at RT and He–1% HF–0.06 H2O gas mixture at 823 K to simulate fluoridation and oxidation in Flibe. The coatings presented suppression of fluoride formation compared with JLF-1 or NIFS-HEAT-2, however weight loss due to WF6 formation was induced, and much Cr2O3 was formed.