Title of article
Flow accelerated corrosion and erosion–corrosion of RAFM steel in liquid breeders
Author/Authors
Kondo، نويسنده , , Masatoshi and Muroga، نويسنده , , Takeo and Sagara، نويسنده , , Akio and Valentyn، نويسنده , , Tsisar and Suzuki، نويسنده , , Akihiro and Terai، نويسنده , , Takayuki and Takahashi، نويسنده , , Minoru and Fujii، نويسنده , , Naoki and Yokoyama، نويسنده , , Yukihiro and Miyamoto، نويسنده , , Hiroshi and Nakamura، نويسنده , , Eiji، نويسنده ,
Issue Information
روزنامه با شماره پیاپی سال 2011
Pages
4
From page
2500
To page
2503
Abstract
Corrosion experiments for RAFM, JLF-1 steel (Fe–9Cr–2W–0.1C) in three types of liquid breeders (i.e. Li, Pb–17Li and Flinak) were performed at 600 °C. The influence of the different experimental parameters, such as a flowing condition, an exposure time and a geometric condition, on the corrosion behavior was investigated. The present study focused on the evaluation of the weight loss of the corroded specimen by the corrosion model based on mass transfer. The dissolution of the metal elements from the steel was accelerated by the fluids. An erosion–corrosion of the steel was caused by the peeling off of the corroded steel surface in the flowing liquid breeders.
Keywords
Erosion–corrosion , Molten salt , Compatibility , Flow accelerated corrosion , Liquid metal