Color agreement between try-in paste and resin cement: Effect of thickness and regions of ultra-translucent multilayered zirconia veneers

Background. The current study aimed at identifying the color agreement between try-in pastes and the respective resin cements and investigated the effect of thickness and regions of Ultra-Translucent Multilayered Zirconia Veneers. Methods. A total of 90 cubic zirconia discs were prepared at two different thicknesses (0.5 mm and 0.7 mm) (n=45) in five groups in terms of the shade of the try-in paste and resin cement as follows: Universal, Clear, Brown, White and Opaque. Try-in paste and the respective resin cement were applied between the specimens and composite substrate, respectively, and colorimetric evaluation was carried out using CIE-Lab system. For each specimen, ΔE between the try-in paste and cement was calculated. Data were analyzed with SPSS 17 using Multifactor ANOVA (P 0.05). Results. Multifactor ANOVA results showed that ΔE values were significantly affected by the resin cement shade and the thickness of ceramic veneer (P 0.05). The results showed better shade agreement between the try-in paste and the respective resin cement with thicker ceramic veneers. The results of Tukey HSD revealed that ΔE values for the Clear, Universal and Brown shades were less than those of the White and Opaque shades. Lighter shades exhibited better agreement between the try-in paste and the respective resin cement. Conclusion. Perceptible color difference was found between the try-in pastes and the respective resin cement in most colors investigated. Although, the agreement of the try-in pastes and the respective resin cement was affected by the thickness of zirconia veneers, the different regions of multilayered ultra-translucent zirconia ceramic showed no significant effect.