Physical Properties of Cuprous Oxide Thin Films Grown on n-Si Substrate by Sol-Gel Spin Coating
Author/Authors
CHE HALIN, D.S. Universiti Kebangsaan Malaysia - School of Applied Physics, Malaysia , TALIB, I.A. Universiti Kebangsaan Malaysia - School of Applied Physics, Malaysia , DAUD, A.R. Universiti Kebangsaan Malaysia - School of Applied Physics, Malaysia , HAMID, M.A.A. Universiti Kebangsaan Malaysia - School of Applied Physics, Malaysia
From page
215
To page
218
Abstract
Cu2O films were grown on n-Si substrates via the sol-gel spin-coating method. The films were annealed under 5% H2 + 95% N2 atmosphere at 350°C, 450°C and 550°C. Diffractogram obtained by the grazing angle x-ray diffractometry showed that the crystallinity of the films increased with increasing annealing temperature. Scanning electron microscopy micrographs revealed that the Cu2O films contain grains of irregular size indicating that the film growth followed the Volmer-Weber growth mode. The micrographs showed the size evolved from irregular shapes with average size of 100 nm at 350°C into rectangular shapes with average size of 200 nm at 550°C. Optical reflectance for 450°C and 550°C film increased gradually at wavelength 480 nm. Higher reflectance for the 450 °C film might be due to better coverage of the film. It also showed that optical absorption occured at wavelength below 480 nm.
Keywords
crystallinity , cuprous oxide , sol , gel , Volmer , Weber growth
Record number
2554716
Link To Document