Magnetic and Structural Studies of Ba0.5Sr0.5(ZnTi)xFei2-2xOi9 Prepared by Ball Milling
Author/Authors
González-Angeles, A. Autonomous University of Baja California - Facultad de Ingenieria, Mexico , Grusková, A. Slovak University of Technology - Faculty of Electrical Engineering and Information Technology, Slovakia , Lipka, J. Slovak University of Technology - Faculty of Electrical Engineering and Information Technology, Slovakia , Sláma, J. Slovak University of Technology - Faculty of Electrical Engineering and Information Technology, Slovakia , Jančárik, V. Slovak University of Technology - Faculty of Electrical Engineering and Information Technology, Slovakia
From page
37
To page
42
Abstract
Results on structural and magnetic studies of Ba0.5Sro.5(ZnTi)xFei2-2xOi9 (where x = 0.2 to 0.6) ferromagnetic powders prepared by mechanical milling are presented. The obtained X-ray diffraction patterns of Zn-Ti substituted (BaSr)0 5M samples showed Magnetoplumbite phase formation for all substituted mixtures; no other secondary phases were detected. Scanning electron microscope analyses reveled that all processed samples possess particle size much below 1 jim and may exhibit promising magnetic and dielectric properties. Magnetic measurements showed that the intrinsic coercivity, Hci, and remanent magnetization, Mr, decreased as the substitution took place, while the saturation magnetization, Ms, remained almost constant (diminution ~ 9%). Hci, decreased from 389.92 down to 171.88 k A/m that represents a 56% drop, whilst Mr registered a fall of ~ 17%
Keywords
Magnetic Studies , Mossbauer Spectroscopy , Ba , Sr , Hexaferrites , Ball Milling
Journal title
Jordan Journal of Physics
Journal title
Jordan Journal of Physics
Record number
2587178
Link To Document