Exploration of high capacity LiNi0.5Mn1.5O4 synthesized by solid-state reaction

LiNi0.5Mn1.5O4 was prepared by an improved solid-state reaction at high heating and cooling rates, the mixed precursors were initially heated up to 900 °C, then directly cooled down to 600 °C and heated for 24 h in air. X-ray diffraction (XRD) pattern shows that LiNi0.5Mn1.5O4 has cubic spinel structure; scanning electron microscopic (SEM) image shows that the particle size is about 0.2 μm together with homogenous distribution. Electrochemical measurements show that LiNi0.5Mn1.5O4 powders delivered up to 143 mAh g−1 with superior cycling performance at the rate of 5/7C.