Study of the performance of Ti–Zr based hydrogen storage alloys

The P–C–I and charging–discharging properties of three Ti–Zr based alloys have been studied. Ni substitution for Mn and Cr in the alloy was found to increase the plateau pressure of the P–C–I curve. In addition, the partial substitution of Cr by V greatly improved the discharge capacity. However, the six-element alloy, Ti0.5Zr0.5V0.2Mn0.7Cr0.5Ni0.6, degraded rapidly in the gas–solid reaction. Hydrogen contents in the alloy under low pressure were increased during hydrogen absorption–desorption cycling. Annealing at 1050°C for 4 h before the P–C–I experiment helped in releasing the retained hydrogen under low pressure. Only a slightly flattened P–C–I slope was obtained for the annealed alloy. Microstructures of the as-cast and annealed alloys were examined and related to the above results. Alloy powder was poisoned after 2-month storage in air, which resulted in the deterioration of discharge capacity. Surface pretreatment on alloy powders by HCl–HF solution decreased the activation time of charge–discharge reaction.