Preparation and properties of carbon nanotube-reinforced vinyl ester/nanocomposite bipolar plates for polymer electrolyte membrane fuel cells

Novel multiwalled carbon nanotubes (MWNTs) were prepared using poly(oxypropylene)-backboned diamines of molecular weights Mw 400 and 2000 to disperse acid-treated MWNTs, improving the performance of composite bipolar plates in polymer electrolyte membrane fuel cells. A lightweight polymer composite bipolar plate that contained vinyl ester resin, graphite powder and MWNTs was fabricated using a bulk molding compound (BMC) process. Results demonstrate that the qualitative dispersion of MWNTs crucially determined the resultant bulk electrical conductivity, the mechanical properties and the physical properties of bipolar plates. The flexural strength of the composite bipolar plate with 1 phr of MWNTs was approximately 48% higher than that of the original composite bipolar plate. The coefficient of thermal expansion of the composite bipolar plate was reduced from 37.00 to 20.40 μm m−1 °C−1 by adding 1 phr of MWNTs, suggesting that the composite bipolar plate has excellent thermal stability. The porosity of the composite bipolar plate was also evaluated. Additionally, the bulk electrical conductivity of the composite bipolar plate with different MWNTs types and contents exceeds 100 S cm−1. The results of the polarization curves confirm that the addition of MWNTs leads to a significant improvement on the single cell performance.