Sorptive Behavior of Monolayer-Protected Gold Nanoparticle Films: Implications for Chemical Vapor Sensing

Monolayer-protected gold nanoparticle materials were synthesized and characterized for use as sorptive layers on chemical sensors. Thiols investigated as monolayer-forming molecules included dodecanethiol, benzenethiol, 4-chlorobenzenethiol, 4bromobenzenethiol, 4-(trifluoromethyl)benzenethiol, 4-hydroxybenzenethiol, and 4-aminobenzenethiol. Films of selected monolayer-protected nanoparticle (MPN) materials were deposited on thickness shear mode devices and vapor uptake properties were measured at 298 K. Many, but not all, MPN-based sensing layers demonstrated rapid and reversible uptake of vapors, and sorptive selectivity varies with the monolayer structure. The mass of vapor sorbed per mass of sorptive material was determined and compared with poly(isobutylene) and poly(epichlorohydrin) as examples of simple sorptive polymers that have been used on vapor sensors. The nanoparticle-based films considered here were less sorptive than the selected polymers on a per-mass basis. Partition coefficients, which measure the mass of vapor sorbed per volume of the sorptive phase, were estimated for these MPN materials and found to be comparable to or less than those of the polymer layers. Implications for the roles of sorption and transduction in determining the performance of chemical sensors coated with nanoparticle-based films are discussed.