Chitosan staple fibers and their chemical modification with some aldehydes

Nine wet-spinning conditions were examined for the preparation of chitosan staple fibers, and novel five N-alkylidene and N-arylidene-chitosan staple fibers were obtained by the post-treatment of the chitosan fibers with aldehydes including vanillin. The tenacity and elongation values of the chitosan filaments were almost unchanged by their post-treatment with monoaldehydes except that with formaldehyde and glyoxal. However, these values decreased significantly in the partially N-modified filaments, which were obtained by the pre-treatment with vanillin. The chitosan filaments (31¯79 mu m in diameter) had a scaly structure on the filament surface as examined by SEM observation.