Effect of phosphorus-ion implantation on the corrosion resistance and biocompatibility of titanium

This work presents data on the structure and corrosion resistance of titanium after phosphorus-ion implantation with a dose of 1017P+/cm2. The ion energy was 25 keV. Transmission electron microscopy was used to investigate the microstructure of the implanted layer. The chemical composition of the surface layer was examined by X-ray photoelectron spectroscopy and secondary ion mass spectrometry. The corrosion resistance was examined by electrochemical methods in a simulated body fluid at a temperature of 37°C. Biocompatibility tests in vitro were performed in a culture of human derived bone cells in direct contact with the materials tested. Both, the viability of the cells determined by an XTT assay and activity of the cells evaluated by alkaline phosphatase activity measurements in contact with implanted and non-implanted titanium samples were detected. The morphology of the cells spread on the surface of the materials examined was also observed. The results confirmed the biocompatibility of both phosphorus-ion-implanted and non-implanted titanium under the conditions of the experiment. As shown by transmission electron microscope results, the surface layer formed during phosphorus-ion implantation was amorphous. The results of electrochemical examinations indicate that phosphorus-ion implantation increases the corrosion resistance after short-term as well as long-term exposures.