Phase transformation of melamine at high pressure and temperature

Pyrolysis experiments of melamine were carried out under high pressure of 5 GPa and different temperatures. The crystal structure, chemical bonding, and composition of the melamine pyrolysate were studied by X-ray diffraction (XRD), Fourier transform infrared spectra (FTIR), X-ray photoelectron spectroscopy (XPS), X-ray energy-dispersive analysis (EDX), and combustion elemental analysis. A new C–N–H phase was found in the pyrolysate at 5 GPa and 800 C. The structure is tentatively indexed as a monoclinic symmetry, with the following lattice parameters: a = 8.5368 (±0.0009)A° , b = 9.1153 (±0.0010)A° , c = 10.2440 (±0.0011)A° , a = c = 90 , and b = 95.5696 (±0.0016) . The photoluminescence behavior of the pyrolysates was investigated. A blue emission at 421 nm for the C–N–H phase was observed under the ultraviolet light excitation of 365 nm.