Pressure vessel steel fracture toughness in the regime from room temperature to 400°C

The fracture toughness of steels that are susceptible to dynamic strain aging shows a minimum at temperatures higher than the upper shelf starting temperature. This phenomenon is caused simultaneously by strain aging and plastic deformation. The first aim of the present work is to analyze the effect of dynamic strain aging on the fracture toughness values of three pressure vessel steels in the temperature range between room temperature and 400°C. Fracture mechanics tests were carried out on A533 GB, A516 G70 and 304L steels to obtain the following parameters: JIC, CTODm and the J-R curves. These values were compared against those available in the present references, and good agreement was found. Charpy V notch tests were also carried out on A516 G70 steel at the same test temperatures as for the fracture mechanics tests to analyze the effect of the strain rate. The critical wide stretch zones of the 304L steel specimens were also measured to verify another authorʹs hypothesis about a toughness drop at the upper shelf temperature.