Hydroxyapatite coating on porous silicon substrate obtained by precipitation process

Hydroxyapatite Ca10(PO4)6(OH)2 (HAP) is known as a bioactive and biocompatible material, HAP coatings were used to improve the biocompatible of substrate by many researcher, In this work, HAP thin films on porous silicon (PS) substrates have been prepared by aqueous precipitation method with rapid thermal annealing (RTA) processes. The HAP films had been prepared under the annealing temperature ranging from 300 to 1000 8C. By the measurement of X-ray diffraction (XRD), it was found that for the crystallinity optimization, the heat-treatment at 850–950 8C for 1 h would be favorable. Atomic force microscopy (AFM) and scanning electron microscope (SEM) measurements reveal a dense and smooth surface of the HAP film, and tightly adherence of the coating on porous silicon substrate after sintered. Thus, by this method, porous silicon could be increased its bioactivity and so that could be used in the biomedical area. # 2004 Elsevier B.V. All rights reserved