The Effects of Load Ratio on Threshold Fatigue Crack Growth of Aluminum Alloys
Author
John C. Duke استاد مشاور , Robert S. Piascik استاد مشاور , Norman E. Dowling استاد راهنما
University
Virginia Polytechnic Institute and state University
Grade
نامعلوم
Major
PhD )Engineering Mechanics(
Number of pages
0
Publish Date
2000
Keyword
Aluminum alloys , Plasticity-induced crack closure , Crack-tip process zone , Microvoids , microcracks , Kmax , Crack-tip damage , Oxide-induced crack closure , Humidity , Load ratio , Fatigue crack closure , Fatigue crack growth , Roughness-induced crack closure , Threshold