The Simultaneous Effect of Graphene and XNBR on the Tensile Properties of Epoxy
پديدآورندگان
Ashenai Ghasemi F. Associate Professor, Faculty of Mechanical Engineering, Shahid Rajaee Teacher Training University, Tehran, 1678815811, Iran , Saberian M. H. saberian1992@yahoo.com Master Student, Faculty of Mechanical Engineering, Shahid Rajaee Teacher Training University, Tehran, 1678815811, Iran , Ghasemi I. Professor, Department of Polymer Processing, Polymer and Petrochemical Institute, Tehran, Iran , Daneshpayeh S. Ph.D. Student, Faculty of Mechanical Engineering, Shahid Rajaee Teacher Training University, Tehran, 1678815811, Iran
تعداد صفحه
2
كليدواژه
Epoxy , Graphene Nano , Platelets , Tensile Properties , Hybrid Nano , Composites.
سال انتشار
1396
عنوان كنفرانس
چهارمين كنفرانس بين المللي دو سالانه مكانيك جامدات تجربي
زبان مدرك
انگليسي
چكيده فارسي
The goal of this study is to investigate the main and simultaneous effects of
graphene nano-platelests (GnPs) and carboxylated nitrile butadiene rubber
(XNBR) on tensile strength and Young’s modulus of epoxy systems. To
evaluate mechanical properties, tensile test was performed in room
temperature. Further, scanning electron microscope (SEM) was used to
observe the state of nano-particles dispersion. The experimental test showed
that the composition include 0.75 wt.% GnPs and 5 wt.% XNBR have the best
mechanical properties among all ternary nano-composites