عنوان مقاله
Morphology of Alpha-Alumina Ceramic Membrane Made by Gelcasting Method
پديدآورندگان
Bahreini Habib Habib.bahreini@yahoo.com Department of Chemical Engineering.Shahreza branch, Islamic Azad University, Shahreza, Iran , Pourmaani Esfahani Narges nargespor1371@gmail.com Department of Chemical Engineering.Shahreza branch, Islamic Azad University, Shahreza, Iran , Ameri Elham ameri@iaush.ac.ir Department of Chemical Engineering.Shahreza branch, Islamic Azad University, Shahreza, Iran
تعداد صفحه
6
كليدواژه
Ceramic membrane , α , Alumina , Ammonium polyacrylate , Gelatin
سال انتشار
1397
عنوان كنفرانس
دومين كنفرانس بين المللي دو سالانه نفت، گاز و پتروشيمي
زبان مدرك
انگليسي
چكيده فارسي
In this work a flat ceramic membrane based on α-alumina was prepared useing gelcasting method. The α-alumina average particle size is 5 μm. Ammonium polyacrylate was used as scattering agent and oral gelatin was utillized as gelatin agent. In this study, the membrane was fabricated as circular disk (58 mm diameter and 2 mm thickness) and subjected for characterization studies using SEM analysis, to evaluate the pore size distribution and membrane structure. Moreover, porosity of the ceramic was obtined 34.28% and shrinkage factor of the membrane was determined.SEM result, showed the micro distribution for pore size of the prepared membrane
كشور
ايران
لينک به اين مدرک