Title Of Article
EFFECTS OF HEAT TREATMENT CONDITIONS AND SLIDING SPEEDS ON THE ADHESIVE WEAR BEHAVIOR OF AISI D6 STEEL
شماره ركورد
16413
Abstract
In this study, effects of wear speeds on the adhesive wear behavior of heat treated AISI D6 steel were investigated. In normalization, steel specimens were austenitized at 900 and 950°C for 30 minutes and then aircooled. Sample was annealed at 850°C for 30 minutes. Adhesive wear tests were performed by pin-on-disc adhesive wear tester under loads of 20 and 40 N at a sliding speeds of 1 and 1.5 m s^-1. Annealed sample showed decreasing adhesive wear resistance and hardness. Adhesive wear resistance and hardness of normalized specimen increased up to 900°C for 30 minutes, but it decreased at 950°C for 30 minutes.
From Page
587
NaturalLanguageKeyword
Adhesive wear , AISI D6 steel , normalizing
JournalTitle
Journal Of The Faculty Of Engineering and Architecture Of Gazi University
To Page
592
JournalTitle
Journal Of The Faculty Of Engineering and Architecture Of Gazi University
Link To Document