orak, ceren ege university - faculty of engineering - department of chemical engineering, İzmir, Turkey , atalay, süheyda ege university - faculty of engineering - department of chemical engineering, İzmir, Turkey , ersöz, gülin ege university - faculty of engineering - department of chemical engineering, İzmir, Turkey
Title Of Article
DEGRADATION OF ETHYLPARABEN USING PHOTO-FENTON-LIKE OXIDATION OVER BiFeO3
شماره ركورد
34342
Abstract
The degradation of ethylparaben using photo-Fenton-like oxidation was investigated in the presence of a BiFeO3 catalyst. Firstly, the catalyst was synthesized using the sol-gel method and characterized via BET and FT-IR analyzes and then, a parametric study was carried out in order to determine the optimum reaction conditions for the degradation of ethylparaben. In this context, the effects of catalyst loading, [H2O2]o, pH, and temperature on the degradation were investigated. According to the results, the optimum reaction conditions were determined for a 5 ppm ethylparaben solution as 0.25 g/L catalyst loading, a pH of 3, and 2 mM [H2O2]o and a 97.7% degradation of ethylparaben was accomplished. Iron leaching at the optimum conditions was evaluated as 1.53 ppm and it is lower than the E.U. iron concentration limitation (2 ppm) in the water. The kinetic study was carried out at the optimum reaction conditions at three different temperatures (25, 35, and 45 °C). The degradation of ethylparaben using photo-Fenton-like oxidation fitted the first order reaction kinetic model. The reaction rate constants were determined as 0.041, 0.050, and 0.069 min^-1 for 25, 35, and 45 °C, respectively. The activation energy was found as 20.4 kJ/mol.
From Page
915
NaturalLanguageKeyword
Ethylparaben , Perovskite , Photo , Fenton oxidation
JournalTitle
Anadolu University Journal of Science and Technology. A : Applied Sciences and Engineering
To Page
925
JournalTitle
Anadolu University Journal of Science and Technology. A : Applied Sciences and Engineering
Link To Document