Electrical Characterizations of $\hbox {MgO}{\hbox {-}}\hbox {ZrO}_{2}$ High Temperature Sol-Gel Insulations Coatings on Different Types of Epoxies

The sol-gel MgO-ZrO₂ electrical insulations were coated on Stainless-Steel-304 (SS) tapes by reel-to-reel process for investigation of electrical properties under various pressure at room temperature (298 K) and liquid nitrogen temperature (77 K) for HTS/LTS high field insert coil. Solutions consist of Mg and Zr based precursors, solvent and chelating agent. The electrical insulation was made on long-length SS substrate. Insulation thickness for 4, 8, and 9 dippings were determined 7, 12, and 13 mum, respectively. Three different types of stycast, 2850 FT/24 LV Black and Blue, and White Buecher Epoxide Resin were studied. Stycast thicknesses were varied from 33-20 mum, when the pressure was applied from 0 to 0.54 GPa. The thicknesses of high temperature insulation coatings and epoxsies were measured by using Environmental Scanning Electron Microscope (ESEM). Resistance, capacitance and High Voltage Breakdown (HV _bd) of the samples were measured by using standard machines Model 6517A Electrometer/High Resistance Meter, 161 analog digital capacitance meter and Model 200-02R High Voltage Power Supply, respectively. The results were presented graphically.