Thin-film polycrystalline Si solar cell on glass substrate fabricated by a novel low temperature process

Thin film polycrystalline Si solar cells on glass substrates were fabricated by the excimer laser annealing of heavily boron doped a-Si and the subsequent deposition of polycrystalline Si on them by plasma-enhanced chemical vapor deposition at low temperature. The resistivity of the boron doped laser annealed polycrystalline Si film reaches to the 2×10^-4 Ω·cm, which shows a strong (111) preferred orientation. The structure of the solar cell presented here is ITO/n μc-Si:H (30 nm)/p poly-Si (2 μm)/p⁺ poly Si (300 nm)/glass substrate, which shows sufficiently high current density despite the low-temperature fabrication. This sufficiently high Jsc is postulated to be both due to the hydrogen passivation of the grain-boundary and the low carrier concentration of poly-Si film by low temperature fabrication