52CR-53NI تاثير ساختار ميكروسكوپي بر جوش پذيري فولاد ريختگي

Microstructural Effect on the Weldability of 25Cr-35Ni Cast Steel

The 25Cr-35Ni heat resistant steel has been Widely used when resistance to oxidation and creep rupture at elevated temperatures is required. In this paper, the microstructural effect on the weldability of this alloy is investigated. The results of this study indicate that this steel has a perfect Weldability in the as cast condition but does not possess good weldability in the aged condition. The as cast microstructure of 25Cr-35Ni steel consists of austenite matrix and a network of primary carbides, while the aged condition consists of austenite matrix and y primary and secondary carbides. The morphological change of primary carbides and the secondary carbides precipitate formation. reducing the elongation and ductility of aged steel, should have enhanced the steel susceptibility to cracking, particularly in the area of the eutectic carbides, and hence, the reduced welt/ability of the steel. The cracking observed was of the intergranular type and spread along the eutectic carbides. It was found that the carbides in the as cast steel consisted of NbC and M23C60 whereas that of the aged steel also exhibited Ni16 iNb8Si7 and M23C6 carbides.