Synergistic inhibitive effect of tartarate and tungstate in preventing steel corrosion in aqueous media

The inhibitive effect of tartarate was studied as a coinhibitor with tungstate in preventing carbon steel corrosion in aqueous solutions. Open circuit potential measurements, weight-loss measurements and polarization studies were conducted to understand the domains of corrosion and passivation. Tartarate ions, even at low concentration, showed excellent synergistic corrosion inhibition characteristics. A mixture of 500 ppm each of the inhibitors was found to be optimum inhibitor combination. This inhibitor combination showed inhibition efficiency as high as 98%. Tartarate in the synergistic inhibitor combination did not reveal any dominant role in shifting the surface potential, even though it showed substantial passivation effect. The present study explores and evaluates the synergistic combination as a potential inhibitor system in combating corrosion on carbon steel surface.