Microstructure and dry-sliding wear resistance of PTA clad (Cr, Fe)7C3/g-Fe ceramal composite coating

Awear resistant (Cr, Fe)7C3/g-Fe ceramal composite coating was fabricated on substrate of a 0.45%C carbon steel by plasma transferred arc (PTA) cladding process using the Fe–Cr–C elemental powder blends. The microstructure, microhardness and dry-sliding wear resistance of the coating were evaluated. Results shown that the plasma transferred arc clad ceramal composite coating has a rapidly solidified microstructure consisting of blocky primary (Cr, Fe)7C3 and the inter-blocky (Cr, Fe)7C3/g-Fe eutectics and is metallurgically bonded to the 0.45%C carbon steel substrate. The ceramal composite coating has high hardness and excellent wear resistance under dry sliding wear test condition