Hydrothermal growth of ZnO on annealed electrodeposited titanate film: Influence of zinc nitrate and methenamine

Hydrothermal growth of hexagonal ZnO nanorods on the annealed titanate nanotube films is reported as a function of molar ratio of Zn(NO3)2 and methenamine (1:1–1:4). The molar ratio of 1:4 results in a dense and thinner rod in comparison with other molar ratios. Corn-like structures of the rods are believed to be due to the higher amine concentration. Raman peaks at 437 and 331 cm 1 are assigned to E2 and E2H–E2L modes. Near band gap edge and green photoluminescence emission indicates the structural and oxygen vacancy. O 1s peak is found built-up of sub-peaks at 530.62, 531.8 and 532.84 eV corresponding to O2 on normal wurtzite structure and OH and oxygen vacancies of ZnO, respectively