Characterization of diamond films deposited on Re substrate by magnetic field-assisted hot filament chemical vapor deposition

A periodically magnetic field (PMF) was used in a hot-filament chemical vapor deposited (HFCVD) for diamond growth on the rhenium substrate. The morphology, band structures and crystalline structure of the film were analyzed by the scanning electron microscopy (SEM), Raman spectroscopy and X-ray diffractometer (XRD), respectively. The results show that the thickness of the diamond film is about 2900 nm by 4 h deposition with magnetic field-assisted. There is no interlayer between diamond film and the rhenium substrate. The result shows that the turn on voltage of the sample is enhanced from 3.3 to 2.6 V/μm with the PMF. Also the total emission current density at 6.2 V/μm increased from 6.3 to 21.5 μA/cm2.