Preparation and characterization of film of poly vinyl acetate ethylene copolymer emulsion

In order to improve the storage modulus and water resistance of poly (vinyl acetate), the vinyl acetate and poly (vinyl alcohol) (PVA) were respectively used as monomers and protective colloid to prepare a new kind of polyvinyl acetate emulsion adhesive by continuous emulsion polymerization. The dynamic mechanics, particle distribution, glass transition temperature, polymer emulsion structure of both polymerized and copolymerized emulsion were analyzed by SEM, DMA and XPS, respectively. The results indicated that the copolymerized emulsion has the appropriate particle size and the uniform particle distribution, the glass transition temperature increased from 50 °C to 70 °C, compared with poly (vinyl acetate). It could be seen from XPS spectra of copolymerized emulsion that key characteristic peak of Cdouble bond; length as m-dashO was still existent. X-ray photoelectron spectra revealed that the addition of EVA did not generate the new bond, whereas the maximum percentage increases in ester was determined in the composite film with the introduction of EVA of 25%, which indicated that the composite film has copolymer structure. The storage modulus and water resistance of poly (vinyl acetate) were improved due to the introduction of the EVA.