Synthesis of porous silicon nano-wires and the emission of red luminescence

This very paper is focusing on the characterization of porous silicon nano-wires prepared via a two-step route, the electroless chemical etching and the following post-treatment of HF/HNO3 solution. Hence, scanning electron microscopy, transmission electron microscopy and confocal fluorescence microscopy are employed for this purpose. From the results of experiments, one can find that the as-prepared silicon nano-wire is of smooth surface and that no visible photo-luminescence emission could be seen. However, the porous structure can be found in the silicon nano-wire treated with HF/HNO3 solution, and the clear photo-luminescence emission of 630 nm can be recorded with a confocal fluorescence microscope. The transmission electron microscopy test tells that the porous silicon nano-wire is made up of a porous crystalline silicon nano-core and a rough coating of silicon oxide. Besides, based on the post-HF- and -H2O2- treatments, the emission mechanism of the red luminescence has been discussed and could be attributed to the quantum confinement/luminescence center model which could be simply concluded as that the electron–hole pairs are mainly excited inside the porous silicon nano-core and then tunneling out and recombining at the silicon oxide coating.