Preparation of high-aspect-ratio ZnO nanorod arrays for the detection of several organic solvents at room working temperature

Chemical sensors based on ZnO nanorod arrays were prepared using chemical bath deposition (CBD) to investigate the sensing performance for the detection of several organic solvents with low concentrations (0.1%, 0.5%, 1%, v/v) at room temperature. High quality and high aspect-ratio (value ∼28) ZnO nanorods have a diameter of about 74 nm and average length of 2.1 μm. Nyquist plots and Bode plots of the ZnO sensors under different organic solvents were obtained by electrical impedance spectroscopy (EIS). The sensing properties such as charge-transfer resistance, double-layer capacitance and dielectric parameters were determined from the impedance spectra to explore the charge transport in low-concentration aqueous solutions. The decreasing trend of the charge-transfer resistance (Rct) as decreasing solvent concentrations is observed, and a straight line at low frequency regime indicates adsorption of water molecules on the oxide surface. The sensitivity of the ZnO sensors was calculated from the resistance variation in target solvents and in deionized water. We demonstrated the use of ZnO nanorod arrays as a chemical sensor capable of generating a different response upon exposure to methanol, ethanol, isopropyl alcohol, acetone and water, wherein the methanol sensing exhibited highest sensitivity. In addition, the ZnO sensor also demonstrates good stability and reproducibility for detection of methanol and ethanol.