Evolution of TiO2 coating layers on lamellar sericite in the presence of La3+ and the pigmentary properties

TiO2-coated sericite powders were prepared by the chemical deposition method starting from lamellar sericite and TiCl4 in the presence or absence of La3+ cations. After calcination at 900 °C for 1 h, the resultant TiO2 nanoparticles on the sericite surfaces existed in anatase phase. The light scattering indexes of the TiO2-coated lamellar sericite powders were dozens of times higher than that of the naked lamellar sericite powders. The presence of La3+ in the deposition solution was beneficial to the formation of the small-sized anatase TiO2 nanoparticles, resulting in the formation of the dense and uniform island-like TiO2 coating layers in a large range of the weight ratios of TiO2 to sericite from 5% to 20%. The TiO2-coated lamellar sericite powders prepared in the presence of La3+ had higher light scattering index than that prepared in the absence of La3+. XPS analysis shows that when La3+ cations were absent in the reaction solution, TiO2 coating layers anchored at the sericite surface via the Ti–O–Si and Ti–O–Al bonds. The presence of La3+ cations caused the formation of Si–O–La and Al–O–La bonds at the sericite surface and Ti–O–La bond at the surface of TiO2 coating layers. After coating TiO2 on the sericite surface, the yellowness of the TiO2-coated sericite powders obviously increased and the brightness slightly decreased.