Characterization and catalytic performance of pure and Li2O-doped CuO/CeO2 catalysts

Pure and Li2O-doped CuO/CeO2 catalysts calcined at 500 °C were prepared by impregnation method. The catalysts are characterized by DTA, TG-DTG, XRD, IR, TEM, nitrogen adsorption at −196 °C and the catalytic decomposition of hydrogen peroxide at 30 °C. The effects of molar ratio, heat treatment time and the doping on the structural, surface and catalytic properties of nanocrystalline Cu/Ce-mixed oxides system have been studied. It was found that the catalytic activity of ceria-supported copper oxide catalysts increased by increasing both the heat treatment time and dopant content. However, the pure Cu/Ce-mixed oxide solids containing 10 wt.% CuO exhibited the best performance. The characterization results indicated that the higher surface area, the formation of solid solution between copper and cerium oxides, and the high dispersion of copper species on the ceria were responsible for the high catalytic activity of the CuO/CeO2 catalysts.