Growth and characterization of Fe nanostructures on GaN

We have investigated the growth of Fe nanostructures on GaN(0 0 0 1) substrates at room temperature using reflection high-energy electron diffraction (RHEED), scanning tunneling microscopy (STM), and superconducting quantum interference device magnetometer. Initially, a ring RHEED pattern appears, indicating the growth of polycrystalline α-Fe. At around 0.5 nm deposition, the surface displays a transmission pattern from α-Fe films with the epitaxial relationship of Fe(1 1 0)//GaN(0 0 0 1) and Fe[1 −1 1]//GaN[1 1 −2 0] (Kurdjumov–Sachs (KS) orientational relationship). Further deposition to 1 nm results in the appearance of a new spot pattern together with the pattern from domains with the KS orientation relationship. The newly observed pattern shows that Fe layers are formed with the epitaxial relationship of Fe(1 1 0)//GaN(0 0 0 1) and Fe[0 0 1]//GaN[1 1 −2 0] (Nishiyama–Wasserman (NW) orientational relationship). From STM images for Fe layers with the KS and NW orientational relationships, it can be seen that Fe layers with the KS relationship consist of round-shaped Fe nanodots with below 7 nm in average diameter. These nanodots coalesce to form nanodots elongating along the Fe[1 0 0] direction, and they have the KS orientational relationship. Elongated Fe nanodots with the NW relationship show ferromagnetism while round-shaped Fe nanodots with the KS relationship show super-paramagnetic behavior. We will discuss their magnetic properties in connection with the change in crystalline configurations of nanodots.