Structure evolution and stoichiometry control of Pb(Zr, Ti)O3 thick films fabricated by electrospray assisted vapour deposition

Well-crystallized and stoichiometric Pb(Zr, Ti)O3 (PZT) films, typically ∼5 μm thick, with pure perovskite-type rhombohedral structures have been successfully prepared via an electrospray assisted vapour deposition (ESAVD) method. Control of the deposition temperature within a narrow range of 300–400 °C resulted in films with the most desirable phases. PZT films with close stoichiometric match with the expected composition ratio and uniform element distribution were obtained by adding the appropriate levels of excess Pb in the precursor solutions. The annealed films were uniform, dense, compact and adherent to the substrates. The dielectric constant, ɛr, and loss tangent, tan δ, of the fabricated PZT films measured at 10 kHz were 442 and 0.09, respectively. The ESAVD deposited PZT films showed a remanent polarization, Pr, of 15.3 μC/cm2 and coercive field, Ec, of 86.7 kV/cm. These results demonstrate the clear potential of the ESAVD method as a promising technique for the fabrication of thick PZT films.